Publications internationales
Résumé: ABSTRACT The concrete equivalent mortar (CEM) method, mainly used in the laboratory, offers a course that facilitates and accelerates experimental test programs with relatively small amounts of materials. To this end, two CEM mixes, with natural and recycled aggregates, at different superplasticizer (SP) concentrations, were tested. The key objective was to investigate how CEM flow property changed at 0, 30, and 60 min of resting time, emphasizing the material’s structuring and destructuring effects. This study describes the flow behaviour of CEMs applying specific tools. Also, a vane-geometry rheometer was used to obtain rheological flow curves. Whatever the SP content in the structuring state, the results indicated reduced flow properties over time. However, an SP content of 1.3% retard the structural buildup property that was not evident at 60 min-rest time. Spread diameters ranging between 300 and 400 mm are measured with the mini cone immediately after mixing. After 60 min of resting time, these diameters were reduced between 260 and 300 mm. Remixing after prolonged rest periods reduces the flow stress values, which decrease from 10 to 18 Pa to 6 to 14 Pa. After a structural build-up at a rest time, the structural break-down effect by remixing re-fluidifies the mixtures. The fluidity has recovered its initial state, reflecting a thixotropic property.
Résumé: The self-compacting concrete (SCC) mix design is much more complex than that of ordinary concrete. Increased testing on fresh concrete and a substantial volume of materials is consequently needed. The concrete equivalent mortar (CEM) method proposes an approach that simplifies and speeds up the experimental testing programmes. This paper seeks to establish the relationships between the rheological properties of SCC and the corresponding CEM mixes. Another aim is to validate the unconventional tools used to test the flow properties of CEM relative to the procedures applied for SCC. Different series of SCC and CEM mixes, based on natural and recycled aggregates, with various superplasticizer contents were tested. The flow behaviour of SCC was tested in line with procedures recommended by EFNARC; that of self-compacting concrete equivalent mortar (SC-CEM) was carried out with unconventional tools (mini-slump cone, slump flow time T250, mini L-Box, 2.5-mm sieve, and mini LCPC Box), described in detail in this paper. A rheometer equipped with vane geometry was also used to show the close relationship between SCC and the SC-CEM yield stress. The experimental results indicate that the fresh properties of the mixture series are congruent with the acceptance criteria of SCC, but they are affected when increasing the superplasticizer dosage and further impacted when recycled coarse aggregates (RCAs) replace natural coarse aggregates (NCAs). The slump flow test appears to be a good practical means for predicting the yield stress of SC-CEM. The cross-referencing results reveal significant relationships between SCC and the corresponding SC-CEM, particularly for filling ability and passing properties. Reasonable correlation coefficients from 0.70 to 0.85 were found.
Publications nationales
Résumé: Cet article présente une étude expérimentale comparative visant à incorporer des granulats grossiers de béton recyclé (GBR) et des granulats grossiers de verre recyclé (GVR) issus de pare-brise usagés dans la composition du béton autoplaçant (BAP). L'objectif principal est d'étudier l'influence de ces granulats sur les propriétés du béton frais et durci. À cette fin, deux séries de mélanges de BAP ont été préparées en remplaçant les granulats grossiers naturels (GGN) par des GBR et les GBR par des GVR. Les propriétés clés du BAP recommandées par les normes et directives européennes (EFNARC) ont été mesurées à l'état frais. La résistance à la compression, l'absorption d'eau et l'observation de la section transversale, afin d'évaluer la stabilité et le potentiel de ségrégation, ont été réalisées sur les bétons durcis. Le remplacement des GGN par des GBR, ainsi que l'utilisation de granulats fins et grossiers de béton recyclé dans le BAP, ne sont pas recommandés, car les critères de fluidité ne peuvent être garantis. Les résultats expérimentaux ont montré que l'essai d'étalement a donné un diamètre de 610 mm. De même, le taux de blocage au L-box était limité à 0,2. Le remplacement des granulats de béton recyclé (RCA) par des granulats de verre recyclé (RGA) n'a pas affecté significativement l'affaissement initial ; les valeurs obtenues sont toutes supérieures au seuil minimal de 650 mm. Le critère de réussite EFNARC est également satisfait. La limite d'élasticité et la viscosité plastique, déterminées par des équations empiriques, concordent avec celles observées pour les bétons autoplaçants (BAP) traditionnels. La résistance à la compression des mélanges BAP-RGA diminue avec l'augmentation de la teneur en verre recyclé, mais reste dans la plage de résistance des BAP. Ces résultats démontrent la possibilité de produire des BAP à partir de granulats de verre de pare-brise usagés